REFORMLUX-204 (C2TES1)
-
About the product : REFORMLUX-204 (C2TES1) highly effective polymer –based, elastic, one - companent, cement based adhesive designed for bonding marble, granite, tiles and seramics, decorative natural stone (mosaic) as well as large facing tiles of this type.
Application areas :
- On the walls and floors of the interior of buildings.
- In outdoor areas.
- When gluing natural stones and marble, not sensitive to water.
- In rooms with underfloor heating water systems, as well as on the floors and walls of refrigeration chambers.
- In gluing new ceramics without removing the old ceramic.
- Applicable in swimming pools, potable water tanks, large swimming pools, walls of industrial and high-rise buildings.
Advantages :
- Elastic, easy to use.
- Only when mixed with water is brought to a ready state.
- Possesses high adhesive ability.
- Easy to apply in both horizontal and vertical directions, does not slip.
- Has a long time of use in the mixed state.
- Slow formation of a thin layer on the surface.
|
AZS 039 (TS 11140) and EN 12004 Very high quality advanced cement-based elastic adhesive developed for decorative natural stone and large cladding materials of this type. |
Application Information |
||
|
Adhesion resistance |
≥ 1 N/mm² |
Using temperature |
(+5°C) - (+30°C) |
|
Adhesion resistance after immersion in water |
≥ 1 N/mm² |
Mixture ratio |
6.5-7.5 liters of water/25 kg |
|
Tensile strength after thermal moistening |
≥ 1 N/mm² |
Duration of use in mixed case |
4 hours |
|
Tensile strength after freeze-thaw |
≥ 1 N/mm² |
Formation of a thin layer on the surface* (For outdoor use) |
an average of 30 minutes |
|
Adhesion resistance |
A1 |
Consumption |
3-5 kg/m² |
|
Resistance after gluing (at least 30 min.) |
≥ 0.5 N/mm² |
Thickness |
3 - 6-8 mm |
|
Slipping |
≤ 0.5 mm² |
Intermediate filler time: On the wall |
24 hours |
|
Transverse deformation |
2.5 mm ≤ S1 ≤ 5 mm |
Intermediate filler time: On the floor |
48 hours |
|
Working temperature |
(-20°C)- (+ 80°C) |
|
|
* These values have been obtained under laboratory conditions (temperature 23°C ± 2, relative humidity 50%) and may vary depending on site application.